FEATURES PROVIDED |
CHEMICAL RESISTANT AND FIRE RETARDING CHARACTERISTICS |
| AHEE |
APPLICATION METHOD |
ROLLER |
| CWZM |
RATED DRYING TIME |
24.000 HOURS NOMINAL |
| CXCY |
PART NAME ASSIGNED BY CONTROLLING AGENCY |
UV RESISTANT EPOXY, LOW SOLAR ABSORBING, HI-SOLIDS, NON-SLIP DECK COATING |
| CZFJ |
VOLATILE ORGANIC COMPOUND IN GRAMS PER LITERS |
215.0 |
| CBGX |
FINISH FOR WHICH FORMULATED |
COARSE |
| FEAT |
SPECIAL FEATURES |
USED ON AIRCRAFT CARRIER FLIGHT DECKS; FIRE RETARDANT IN CURED STATE; VOLUME SOLIDS 78.0 PERCENT; MUST PRE-MIX BASE MATERIAL AND HARDNER; POT LIFE 4.0 HOURS AT 70.0 DEG. F; CURE TIME FOUR DAYS AT 70.0 DEG. F; ESTIMATED COVERAGE 25-30 SQUARE FT. PER GALLON WITH ROLLER, 18-22 SQUARE FT. PER GALLON WITH NOTCHED TROWEL; WEIGHT 18.7 POUNDS PER GALLON; FLASH POINT 102 DEG. F. COMPLETLY CURED; RESULTS OF COEFFICIENT OF STATIC FRICTION TEST IN ACCORDANCE WITH MIL-PRF-24667A, 500 CYCLE TEST ARE 1.22 (DRY) AND 1.20 (WET); PACKAGED IN 5.0 GALLON KITS |
| HUES |
COLOR |
GRAY, DARK |